Mostrar el registro sencillo del ítem

dc.contributor.advisorCano Cuadro, Heidis Patriciaspa
dc.contributor.advisorSabau, Marianspa
dc.contributor.authorQuecedo Llinás, Luis Pablospa
dc.date.accessioned2020-09-15T00:10:17Z
dc.date.available2020-09-15T00:10:17Z
dc.date.issued2020
dc.identifier.citationQuecedo, L. (2020). Comportamiento a la corrosión de varillas ½” grado 60 mediante ensayos acelerados de cámara de niebla salina. Trabajo de Pregrado. Recuperado de https://hdl.handle.net/11323/7100spa
dc.identifier.urihttps://hdl.handle.net/11323/7100spa
dc.description.abstractIn this paper was studied the behavior, regarding to the corrosion, in this case ½” grade 60 rebars were used. Prior this, the chemical composition of the rebars was studied, founding carbon, manganese and copper as the most predominant elements. An accelerated test in a salt spray chamber was realized, where the rebars were exposed for periods of 1, 3 and 7 days, the test was performed according to ASTM B-117:2019 standard. Afterward the corrosion rate of the rebars according to ISO 9226:2012 standard was estimated and the corrosion rate-time curve was made, noticing a high corrosion rate the first day which decreased with the course of the test .Also characterization test were performed, a tensile test was carried out in the universal testing machine then with the results, stress-strain graphic was realized, later an optical microscopy test was made and the inner structure of the rebar was analyzed observing a ferrite and perlite microstructure in the transverse and longitudinal cuts, besides an X-ray diffraction (XDR) test was carried out with which an X-ray diffractogram was made and the characteristic peaks of the corrosion products found were analyzed, in such peaks were found lepidocrocite in 2θ de 15.12° y 2θ es 46.15, also in 2θ de 35.25° akageneite was found. Also, the scanning electron microscopy was performed with which the products morphology was observed, it was possible to see granular, globular and laminar formations of lepidocrocite, as well tubular formations corresponding to akageneite were found. It was concluded that the corrosion rate had high values the first days which decreased when the rebars get more mass, such values indicated that the corrosion was increasing with the course if the days, but in a lower rate. An orange coloration typical of the lepidocrocite presence in high chloride environments was found. Also, corrosion products corresponding to high chloride environments or simulated environments such the case of akageneite was found.spa
dc.description.abstractEn este trabajo se estudió el comportamiento que tienen las varillas de acero con respecto a la corrosión, en este caso la varilla de ½” grado 60. Para ello previamente se estudió la composición química de las varillas en las que se halló carbono, manganeso y cobre como los elementos con mayor predominancia. Se realizó una prueba acelerada en cámara de niebla salina en la cual se expusieron las barras por periodos de 1, 3 y 7 días, dicha prueba fue llevada a cabo bajo la normativa ASTM B-117:2019. Posteriormente se llevó a cabo la estimación de la velocidad de corrosión de las varillas cual fue realizada de acuerdo a la norma ISO 9226:2012 y se realizó la curva de velocidad de corrosión vs tiempo, notándose una gran velocidad de corrosión el primer día el cual decreció con el desarrollo de la prueba. Posteriormente se realizaron pruebas de caracterización, en los que se llevó a cabo el ensayo tracción en la máquina universal de ensayos y con los resultados se realizó la gráfica esfuerzo vs deformación, luego se realizó el ensayo de microscopia óptica en el cual se analizó la estructura interna de las varillas y donde se observó una microestructura de ferrita y perlita en los cortes transversales y longitudinales, además se realizó el ensayo de difracción de rayos X (DRX) con el que se realizó un difractograma de rayos X y se analizaron los picos característicos de los productos de corrosión, en dichos picos se encontró la lepidocrocita en los ángulos 2θ de 15.12° y 2θ es 46.15, además de la akaganeíta en el ángulo 2θ es 35.25. Por último, se realizó el ensayo de microscopía electrónica de barrido (SEM) con el cual se observó la morfología de los productos encontrados observándose lepidocrocita con forma granular, globular, laminar, de igual forma se observó akaganeíta con forma tubular. Se concluyó que la velocidad de corrosión tuvo valores elevados los primeros días los cuales disminuyeron a medida que las varillas ganaron masa, dichos valores indicaron que la corrosión en la varilla aumentaba con el paso de los días, pero a un ritmo menor. Se encontró una coloración principalmente anaranjada típica de la presencia de lepidocrocita los tres días de estudio en las varillas. Además, se encontraron productos de corrosión que corresponden a ambientes con alto contenido de cloruros o en ambientes simulados como es el caso de la akaganeíta.spa
dc.language.isospa
dc.publisherCorporación Universidad de la Costaspa
dc.rightsAttribution-NonCommercial-ShareAlike 4.0 Internationalspa
dc.rights.urihttp://creativecommons.org/licenses/by-nc-sa/4.0/spa
dc.subjectCorrosionspa
dc.subjectSalt spray Chamberspa
dc.subjectLepidocrocitespa
dc.subjectAkaganeitespa
dc.subjectCorrosiónspa
dc.subjectCámara de niebla salinaspa
dc.subjectLepidocrocitaspa
dc.subjectAkaganeítaspa
dc.titleComportamiento a la corrosión de varillas ½” grado 60 mediante ensayos acelerados de cámara de niebla salinaspa
dc.typeTrabajo de grado - Pregradospa
dc.rights.accessrightsinfo:eu-repo/semantics/openAccessspa
dc.identifier.instnameCorporación Universidad de la Costaspa
dc.identifier.reponameREDICUC - Repositorio CUCspa
dc.identifier.repourlhttps://repositorio.cuc.edu.co/spa
dc.publisher.programIngeniería Civilspa
dc.relation.referencesAmerican Society for Testing and Materials (ASTM B117) (2019). American Society for Testing and Materials. Recuperado el 09 de Marzo de 2020, de https://www.astm.org/Standards/B117.htmspa
dc.relation.referencesInternational Organization for Standardization (ISO9226). (2012). International Organization for Standardization. Recuperado el 01 de Marzo de 2020, de https://www.iso.org/standard/53502.htmlspa
dc.relation.referencesInternational Organization for Standardization (ISO9223). (2012). International Organization for Standardization. Recuperado el 01 de Marzo de 2020, de https://www.iso.org/standard/53499.htmlspa
dc.relation.referencesBaorong H., Xiaogang L., Xiumin M., Cuiwei D., Dawei Z., Meng Z., Weichen X., Dongzhu L., & Fubin M. (2017). The cost of corrosion in China. npj Mater Degrad 1, 4 (2017). https://doi.org/10.1038/s41529-017-0005-2spa
dc.relation.referencesXiaogang L.,Dawei Z.,Zhiyong L.,Zhong L.,Cuiwei D.,Chaofang D. (2015). Materials science: Share corrosion data to prevent disasters, Xiaogang Li and colleagues call for open data infrastructures to collate information on materials failures. Nature News, 527, 441–442.spa
dc.relation.referencesKoch G., Varney J., Thompson N., Moghissi O., Gould M., Payer J. (2016). International measusres of prevention, application, and economics of corrosión technologies study. NACE International.spa
dc.relation.referencesPapadopoulos M., Apostolopoulos C., Zervaki A., Haidemenopoulus G. (2011). Corrosion of exposed rebars, associated mechanical degradation and correlation with accelerated corrosion tests. Construction and Building Materials, 25(8), 3367-3374. https://doi.org/10.1016/j.conbuildmat.2011.03.027.spa
dc.relation.referencesAlmusallam A. (2001). Effect of degree of corrosion on the properties of reinforcing steel bars. Construction and Building Materials, 15(8), 361-368. https://doi.org/10.1016/S0950- 0618(01)00009-5spa
dc.relation.referencesMontoya P., Díaz I., Graniz N., De la Fuente D., Morcillo M. (2013). An study on accelerated corrosion testing of weathering steel. Materials Chemistry and Physics, 142(1), 220-228. http://dx.doi.org/10.1016/j.matchemphys.2013.07.009.spa
dc.relation.referencesWu H., Lei H., Chen F., Quiao J. (2019). Comparison on corrosion behaviour and mechanical properties of structural steel exposed between urban industrial atmosphere and laboratory simulated environment. Construction and Building Materials, 211, 228-243. https://doi.org/10.1016/j.conbuildmat.2019.03.207.spa
dc.relation.referencesAustin S., Lyons R., Ing M. (2004). Electrochemical Behavior of Steel-Reinforced Concrete During Accelerated Corrosion Testing. CORROSION, 60(2), 203-212. https://doi.org/10.5006/1.3287722.spa
dc.relation.referencesLiu M., Cheng X., Li X., Hu J., Pan Y., Jin Z. (2016). Indoor accelerated corrosion test and marine field test of corrosion-resistant low-alloy steel rebars. Case Studies in Construction Materials, 5, 87- 99. https://doi.org/10.1016/j.cscm.2016.09.005.spa
dc.relation.referencesMontoya P., Granizo N., De la Fuente D., Morcillo M., (2007). Evaluación y caracterización de la herrumbre de aceros autoprotectores (patinables) obtenida en diferentes ensayos acelerados de corrosión. Scientia Et Technica, 13(36), 531-536.spa
dc.relation.referencesPapadopoulos M., Apostolopoulos C., Alexopoulos N., Pantelakis S. (2007). Effect of salt spray corrosion exposure on the mechanical performance of different technical class reinforcing steel bars. Materials & Design, 28(8), 2318-2328. https://doi.org/10.1016/j.matdes.2006.07.017.spa
dc.relation.referencesCalero J., Alcántara J., Díaz I., Simancas J., De la Fuente D., Morcillo M. (2017). Wet/dry accelerated laboratory test to simulate the formation of multilayered rust on carbon steel in marine atmospheres. Corrosion Engineering, Science and Technology, 52(3), 178-187. https://doi.org/10.1080/1478422X.2016.1244619.spa
dc.relation.referencesArtigas A., Monsalve., Sipos K., Bustos O., Mena J., Seco R., Garza-Montes-de-Oca N. (2015). Development of accelerated wet–dry cycle corrosion test in marine environment for weathering steels. Corrosion Engineering, Science and Technology, 50(8), 628-632. https://doi.org/10.1179/1743278215Y.0000000007.spa
dc.relation.referencesGonzalez J. (1989), Control de la corrosión: estudio y medida por técnicas electroquímicas. Madrid, España: Consejo superior de investigaciones científicas centro nacional de investigaciones metalúrgicas.spa
dc.relation.referencesMorcillo M., Gonzalez B. (2018). La corrosión atmosférica del acero al carbono en ambientes costeros. Madrid, España: Consejo superior de investigaciones científicas centro nacional de investigaciones metalúrgicas.spa
dc.relation.referencesNavarrete C., Salgado E., Celinda O. (2007). Determinación de la corrosividad atmosférica de las ciudades de Santo Domingo y Esmeraldas. Quito: QUITO/ EPN/ 2007.spa
dc.relation.referencesPeña A., Rendón H. (2013). Guía y tablas técnicas de los aceros. Medellín, Colombia: Ferrocortes S.A.S.spa
dc.relation.referencesMorcillo M., De la Fuente D., Díaz I., Cano H. (2011). Atmospheric corrosion of mild Steel. Revista de metalurgia, 47(5). 10.3989/revmetalm.1125spa
dc.relation.referencesLeón-Bello F., Amaya-Malpica M. (2008). Acción galvánica superficial en una matriz de acero al carbono constituida por microceldas con granos de ferrita y perlita. Revista mexicana de ingeniería química. 7(1), 29-33.spa
dc.type.coarhttp://purl.org/coar/resource_type/c_7a1fspa
dc.type.contentTextspa
dc.type.driverinfo:eu-repo/semantics/bachelorThesisspa
dc.type.redcolhttp://purl.org/redcol/resource_type/TPspa
dc.type.versioninfo:eu-repo/semantics/acceptedVersionspa
dc.type.coarversionhttp://purl.org/coar/version/c_ab4af688f83e57aaspa
dc.rights.coarhttp://purl.org/coar/access_right/c_abf2spa


Ficheros en el ítem

Thumbnail
Thumbnail

Este ítem aparece en la(s) siguiente(s) colección(ones)

Mostrar el registro sencillo del ítem

Attribution-NonCommercial-ShareAlike 4.0 International
Excepto si se señala otra cosa, la licencia del ítem se describe como Attribution-NonCommercial-ShareAlike 4.0 International