Reemplazo del agregado fino por escoria de horno de cubilote para la fabricación de concreto

Replacing fine aggregate for cupola furnace slag in concrete


Thumbnail
View/Open
Reemplazo del agregado fino por escoria de horno de cubilote para la fabricación de concreto (743.4Kb)
Date
2014-07-01
Author
Cruz Hernández, Ricardo Alfredo
Franco Durán, Diana Marcela
Pérez Bustos, Ludwing
Metadata
Show full item record
BASE GoogleScholar
Compartir:


Impacto

URI: http://hdl.handle.net/11323/2607

Abstract

Este trabajo presenta las propiedades físico-mecánicas obtenidas de un concreto fabricado con escoria de horno de cubilote (EHC), la cual se utilizó como sustituto del agregado fino (arena) en diferentes proporciones: 0, 10, 15 y 20 %. La evaluación de la granulometría, densidad, absorción, humedad natural y contenido de material férrico de la EHC permitió caracterizarla como arena gruesa bien gradada, con poca cantidad de finos. Para una resistencia de diseño de 14 MPa del concreto modificado (CM) se realizaron ensayos de resistencia a la compresión, módulo de rotura, absorción, módulo de elasticidad y densidad de material endurecido. Los resultados obtenidos evidencian un comportamiento favorable del CM en su resistencia a compresión, al sustituir el 20 % de arena por escoria. Asimismo, se encontró que la densidad mantiene una relación proporcional con el porcentaje de sustitución y el valor de su masa unitaria se encuentra dentro del rango de valores aceptable para un concreto de peso normal.
 
This study presents the physical-mechanical properties of concrete made with crushed cupola furnace slag (CFS). The sand (fine aggregate) was replaced for CFS in differ-ent proportions: 0, 10, 15 and 20%. Granulometry, density, absorption, natural moisture and iron content evaluation showed CFS as well-graded sand with the right thickness and little quantity of fine grains. The modified concrete (MC) de-sign strength was 14 MP. For each percentage of substitution, tests such as compressive strength, modulus of rupture, absorption, tensile strength, modulus of elasticity, and hardened material density were carried out. As a result, 20 % slag MC showed a favorable behavior in compressive strength. Likewise, density is proportional to the substitution percentage and its unit mass value is within the range of acceptable values for a nor-mal concrete weight
 
Para citar este documento con norma APA sexta edición utilice:
Cruz Hernández, R., Franco Durán, D., & Pérez Bustos, L. (2014). Reemplazo del agregado fino por escoria de horno de cubilote para la fabricación de concreto. INGE CUC, 10(1), 83-88. Recuperado a partir de https://revistascientificas.cuc.edu.co/ingecuc/article/view/347

Collections
  • Revistas Científicas

Browse

All of RedicucCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

My Account

Login

Compartir en

Universidad de la Costa, CUC

  • Calle 58 # 55 - 66. Barranquilla, Colombia

  • 336 22 00

  • repositorioredicuc@cuc.edu.co

Corporación Universidad de la Costa CUC, Personería Jurídica con Resolución No. 352 del 23 de abril de 1971 y reconocida como Universidad mediante resolución 3235 del 28 de marzo de 2012 expedida por el MEN. Institución de Educación Superior sujeta a inspección y vigilancia por el Ministerio de Educación Nacional.

Enlaces institucionales:

  • Universidad de la Costa
  • Biblioteca
  • Catálogo bibliográfico
  • Recuperador Primo

Universidad de la Costa CUC.
Politica de Protección de Datos.