Caracterización mecánica y química del sistema Mortero-Poliurea

Thumbnail
View/Open
Trabajo de grado (3.075Mb)
Date
2018-10-27
Author
Vásquez Suarez, Loraine Isabel
Metadata
Show full item record
BASE GoogleScholar
Compartir:


Impacto

URI: http://hdl.handle.net/11323/466

Abstract

En este trabajo de investigación se prepararon morteros poliméricos adicionando distintos porcentajes de poliurea (2, 4 y 5 %) y evaluando sus propiedades mecánicas y estructurales mediante ensayos de compresión y microscopia electrónica de barrido (SEM) y comparándolas frente a un mortero control. Los resultados indicaron que existen dos factores que influyen en las propiedades del sistema, el tamaño de partícula y la cantidad de polímero adicionado, observándose una mayor resistencia a menor porcentaje de adición de poliurea y a menor tamaño de partícula. Bajo estas condiciones y tras la maduración del sistema a los 28 días, estos morteros poliméricos superan hasta en un 20% las propiedades mecánicas a compresión de los morteros de pega tradicionales. Esto probablemente sea consecuencia de la mejor adherencia alcanzada en la cicatriz polímero/cemento hidratado y a la menor cantidad de poros generados evitando la propagación de micro fisuras.
 
In this research work, polymer mortars were prepared by adding different percentages of polyurea (2, 4 and 5%) and evaluating their mechanical and structural properties through compression tests and scanning electron microscopy (SEM) and comparing them against a control mortar. The results indicated that there are two factors that influence the properties of the system, the particle size and the amount of polymer added, with greater resistance being observed at a lower percentage of polyurea addition and a smaller particle size. Under these conditions and after the maturation of the system at 28 days, these polymer mortars exceed up to 20% the mechanical compression properties of traditional glue mortars. This is probably a consequence of the better adhesion achieved in the hydrated polymer / cement scar and the lower amount of pores generated, avoiding the propagation of micro cracks.
 
Collections
  • Pregrado

Browse

All of RedicucCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

My Account

Login

Compartir en

Universidad de la Costa, CUC

  • Calle 58 # 55 - 66. Barranquilla, Colombia

  • 336 22 00

  • repositorioredicuc@cuc.edu.co

Corporación Universidad de la Costa CUC, Personería Jurídica con Resolución No. 352 del 23 de abril de 1971 y reconocida como Universidad mediante resolución 3235 del 28 de marzo de 2012 expedida por el MEN. Institución de Educación Superior sujeta a inspección y vigilancia por el Ministerio de Educación Nacional.

Enlaces institucionales:

  • Universidad de la Costa
  • Biblioteca
  • Catálogo bibliográfico
  • Recuperador Primo

Universidad de la Costa CUC.
Politica de Protección de Datos.