Influencia de la calidad del agua subterránea en la resistencia a la compresión de morteros hidráulicos

Abstract

In this research work, hydraulic mortar cubes were prepared, using groundwater to prepare the mixture, evaluating its resistance through compression tests and comparing them against control mortar cubes prepared with drinking water. The results indicated that the groundwater used is suitable as water for concrete, since the average resistance of the mortar cubes made with this type of water was 96.5% resistance at 7 days with respect to the standard sample, thus being within the limits allowed by NTC 3459; On the other hand, when characterizing drinking water and groundwater, it was observed that these two types of water have similar values in most of the physicochemical parameters measured, except in dissolved oxygen and hardness.

En este trabajo de investigación se prepararon cubos de mortero hidráulico, utilizando agua subterránea para la elaboración de la mezcla, evaluando su resistencia mediante ensayos de compresión y comparándolos frente a cubos de mortero de control preparados con agua potable. Los resultados indicaron que el agua subterránea utilizada es apta como agua para concretos , ya que el promedio de las resistencias de los cubos de mortero elaborados con este tipo de agua fue de un 96,5% de resistencia a los 7 días con respecto a la muestra patrón , encontrándose así dentro de los límites permisibles por la norma NTC 3459; por otra parte al caracterizar el agua potable y el agua subterránea, se pudo observar que estos dos tipos de agua poseen valores similares en la mayoría de los parámetros fisicoquímicos medidos, excepto en el oxígeno disuelto y la dureza.